TORAYCA® laminate method - Specifications/performance
TORAYCA® laminate performance table
| TORAYCA® laminate part number | TL510 | TL515 | TL520 | Remarks |
|---|---|---|---|---|
| CFRP sheet thickness*1 (mm) | 1.0 | 1.5 | 2.0 | |
| CFRP sheet width (mm) | 50.0 | |||
| Density*1 (g/cm3) | 1.60 | Density of CF 1.80g/cm3 | ||
| Product weight*1 (g/m) | 80 | 121.5 | 160 | |
| CF weight per unit length (g/m) | 60 | 90 | 120 | |
| CF weight per unit area (g/m2) | 1,200 | 1,800 | 2,400 | |
| Tensile strength*1, *2 (kN/mm2) (kgf/cm2) |
2.4 24400 |
Tensile strength of CF4.9 kN/mm2 | ||
| Young's modulus*1, *2 (kN/mm2) (kgf/cm2) |
167 1.70×106 |
Young's modulus of CF 230 kN/mm2 | ||
- *1: Performance value that takes resin into account. The carbon fiber yarn used is TORAYCA® T700S.
- *2: The tensile strengths and Young's modulus are based on internal data.
TORAYCA® laminate performance table
| Test item | Units | Internal standard value | Test method/conditions |
|---|---|---|---|
| Sikadur 30 | |||
| Vertical droop (mixture) | No drooping allowed. | JISA 5758 (20°C) | |
| Density (after cured) | g/cm3 | 1.9±0.1 | JIS K 7112(20°C) |
| Usable time | min | 60 or more(20°C) | Temperature raising method |
| Compression yield strength | N/mm2（kgf/cm2） | 68.6 (700) or more | JIS K 7208 (20°C/7 days) |
| Bending strength | N/mm2（kgf/cm2） | 49.0 (500) or more | JIS K 7203 (20°C/7 days) |
| Tensile strength | N/mm2（kgf/cm2） | 19.6 (200) or more | JIS K 7113 (20°C/7 days) |
| Compressive modulus of elasticity | N/mm2（kgf/cm2） | 3,920 (40,000) or more | JIS K 7208 (20°C/7 days) |
| Tensile shear strength* | N/mm2（kgf/cm2） | 9.8 (100) or more | JIS K 6850 (20°C/7 days) |
| Impact strength | KJ/mm2（kgf/cm2） | 1.47 (1.5) or more [measured at 20°C] | JIS K 7111 (20°C/7 days) |
| Hardness (Shore D) | HDD | 80 or more | JIS K 7215 (20°C/7 days) |
| Mixing ratio (weight) | Base compound (A):Curing agent (B) = 3:1 Base compound (white) x curing agent (black) = Gray |
||
- * Solvent-free type.
- * Product of Sika Ltd.
- * For use all year round (provided that the temperature is 5°C or above).
- * When applying the material on wet surface, rub the material into the base completely.
- * Evaluate with a scale (sandblasting). Guideline for conversion to the international unit system (SI): 1 kgf = 9.8 N, 1 cP = 1 mPas, 1 kgfcm = 9.8 x 10-2J
Updated August 3, 2021
Version Original