TORAYCA™ Fabrics Method Specifications/Performance
Specifications and Performance of Civil Engineering Fabrics
| Product No. | UT70 -20G |
UT70 -30G |
UT70 -40G |
UT70 -45G |
UT70 -60G |
UM46 -30G |
UM46 -34G |
UM46 -40G |
BT70 -20 |
BT70 -30 |
||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Type | Uni-directional high-strength cloth | Uni-directional medium-elasticity cloth | Bi-directional high-strength cloth | |||||||||
| Maintenance weight (g/m2) |
200 | 300 | 400 | 450 | 600 | 300 | 340 | 400 | 100 lengthwise 100 widthwise |
150 lengthwise 150 widthwise |
||
| Sheet thickness (mm) *1 |
0.111 | 0.167 | 0.222 | 0.25 | 0.333 | 0.163 | 0.185 | 0.217 | 0.056 lengthwise 0.056 widthwise |
0.083 lengthwise 0.083 widthwise |
||
| Density(g/cm3) | 1.8 | 1.8 | 1.8 | 1.8 | 1.8 | 1.84 | 1.84 | 1.84 | 1.8 | 1.8 | ||
| Tensile strength | (kN/mm2) | 3.4 | 3.4 | 3.4 | 3.4 | 3.4 | 2.4 | 2.4 | 2.4 | 2.9 lengthwise 2.9 widthwise |
2.9 lengthwise 2.9 widthwise |
|
| (kgf/cm2) | 35000 | 35000 | 35000 | 35000 | 35000 | 25000 | 25000 | 25000 | 30,000 lengthwise 30,000 widthwise |
30,000 lengthwise 30,000 widthwise |
||
| Young's modulus | Construction *2 | (kN/mm2) | 230 | 230 | 230 | 230 | 230 | 440 | - | - | 230 | 230 |
| (kgf/cm2) | 2.34×106 | 2.34×106 | 2.34×106 | 2.34×106 | 2.34×106 | 4.5×106 | - | - | 2.34×106 | 2.34×106 | ||
| Civil engineering *3 | (kN/mm2) | 245 | 245 | 245 | 245 | 245 | 440 | 440 | 440 | 245 | 245 | |
| (kgf/cm2) | 2.5×106 | 2.5×106 | 2.5×106 | 2.5×106 | 2.5×106 | 4.5×106 | 4.5×106 | 4.5×106 | 2.5×106 | 2.5×106 | ||
| Width(cm) | 25,33,50 | 25,33,50 | 25,33,50 | 50 | 50 | 25 | 25 | 25 | 100 | 100 | ||
- *1. Value measured from the actual cross-section area of carbon fiber. The thickness of applied material including resin is 0.6 to 1.5 mm per layer.
- *2. Young's modulus specified in "Design/Application Guidelines for Antiseismic Retrofitting of Existing Reinforced Concrete Structures and Steel-framed Reinforced Concrete Structures Using Continuous Fiber Reinforcement Material" by the Japan Building Disaster Prevention Association, dated September 1999.
- *3. Carbon Fiber Restore/Reinforcement Technology Work Group, Structure & Bridge Laboratory, Civil Engineering Research Center, Ministry of Construction. Young's modulus specified in "Joint Research Report on Restore/Reinforcement of Concrete Members (III) - Design/Application Guidelines on Restore/Reinforcement of Road Bridge Concrete Members by Carbon Fiber Sheet Bonding Method (Draft)-" dated December 1999.
- - Tensile strength represents a characteristic value of material strength, while Young's modulus represents an average.
- - Special weave shifting treatment prevents the yarn from coming loose easily when cut.
- - The package contains one 50-m roll.
Primer Specifications and Performance
| Product No. | For spring/summer/fall | For winter | Remarks |
|---|---|---|---|
| TSP400S | TSP400W | ||
| Usable time | 60 minutes (20°C) | 90 minutes (10°C) | Temperature raising method (300g) |
| Specific gravity * | 1.00 to 1.30 (20°C) | JIS K7112 | |
| Tensile shear Adhesive strength |
10 MPa or more (20°C) | JIS K6850 | |
| Adhesive strength | 1.5 MPa or more (20°C) | JIS A6909 | |
| Operating temperature | 15°C to 35°C | 5°C to 20°C | - |
| Blend ratio | Main agent : Curing agent = 2 : 1 | - | |
| Shipping unit | 10kg | ||
| JAIA F☆☆☆☆ obtained Non-formaldehyde registration number |
◎TSP400S 009198 |
| ◎TSP400W 009199 |
- * SR-CF method specified material
Specifications and Performance of Irregularity Correction Material (Putty)
| Product No. | For spring/summer/fall | For winter | Remarks |
|---|---|---|---|
| TSF600S | TSF600W | ||
| Usable time | 90 minutes (20°C) | 90 minutes (10°C) | Temperature raising method (300g) |
| Specific gravity | 1.30 to 1.50 (20°C) | JIS K7112 | |
| Tensile shear Adhesive strength |
10 MPa or more (20°C) | JIS K6850 | |
| Adhesive strength | 1.5 MPa or more (20°C) | JIS A6909 | |
| Operating temperature | 15°C to 35°C | 5°C to 20°C | - |
| Blend ratio | Main agent : Curing agent = 2 : 1 | - | |
| Shipping unit | 10kg | ||
| JAIA F☆☆☆☆ obtained Non-formaldehyde registration number |
◎TSF600S 009200 |
| ◎TSF600W 009201 |
- * SR-CF method specified material
Specifications and Performance of Impregnated Adhesive Resin
| Product No. | For spring/summer/fall | For winter | Remarks |
|---|---|---|---|
| TSR800S | TSR800W | ||
| Usable time | 45 minutes (20°C) | 60 minutes (10°C) | Temperature raising method (300g) |
| Specific gravity of cured resin | 1.00 to 1.30 (20°C) | JIS K7112 | |
| Bending strength | 40 MPa or more (20°C) | JIS K7203 | |
| 40 MPa or more (20°C) | 30 MPa or more (20°C) | JIS K7113 | |
| Tensile shear Adhesive strength |
10 MPa or more (20°C) | JIS K6850 | |
| Operating temperature | 15°C～35°C | 5°C～20°C | - |
| Blend ratio | Main agent : Curing agent = 2 : 1 | - | |
| Shipping unit | 10kg | ||
| JAIA F☆☆☆☆ obtained Non-formaldehyde registration number |
◎TSR800S 009202 |
| ◎TSR800W 009203 |
- * SR-CF method specified material
Specifications and Performance of Void Filling Adhesive Resin (Resin for SR-CF Method)
| Product No. | For spring/summer/fall | For winter | Remarks |
|---|---|---|---|
| AR200S | AR200W | ||
| Usable time | 60 minutes (20°C) | 60 minutes (5°C) | Temperature raising method (300g) |
| Specific gravity | 1.00 to 1.40 (20°C) | JIS K7112 | |
| Bending strength | 40 MPa or more (20°C) | JIS K7203 | |
| 40 MPa or more (20°C) | 20 MPa or more (20°C) | JIS K7113 | |
| Impact strength | 1.5kJ/m2 or more (20°C) | JIS K7111 | |
| Hardness | 80 HDD or more (20°C) | JIS K7215 | |
| Tensile shear Adhesive strength |
10 MPa or more (20°C) | JIS K6850 | |
| Operating temperature | 15°C to 35°C | 5°C to 20°C | - |
| Blend ratio | Main agent : Curing agent = 2 : 1 | - | |
| Shipping unit | 6kg | ||
| JAIA F☆☆☆☆ obtained Non-formaldehyde registration number |
◎AR200S 009204 |
| ◎AR200W 009205 |
- * SR-CF method specified material
- * AR200 is not a low-odor type.